Carbon Fiber Papers can be used as gas diffusion substrates or electrode backing for fuel cell applications. The table below lists nominal properties of commercially available AvCarb Carbon Papers for fuel cells. Please contact us for assistance in selecting the right product for your application or for more information.
Features:
1.Offer many types of GDLs for different operating conditions.
2.GDL can be customized for specific operating conditions.
A.with Micro Porous Layer
Substrate with MPL&PTFE |
Carbon paper |
|||||
Measurement |
Units | Method | N1S1007 | GDL240 | GDL260 | GDL340 |
Thickness |
mm | TECLOCK SM-114 | 0.21 | 0.24 | 0.26 | 0.34 |
Basic weight |
g/m2 | ASTM D-646 | 85 | 90 | 100 | 125 |
Air permeablity |
sec | Gurley |
<225 |
<85 |
<200 |
<200 |
Through-Plane Resistance |
mΩcm2 | Base on ASTM C-611 |
<15 |
<15 |
<10 |
<10 |
Tensile Strength(MD) |
N/cm | ASTM D-828 | 35 | 30 | 37 | 45 |
Tensile Strength(XD) |
N/cm | 17 | 18 | 33 | 36 | |
Flexural Modulus(MD) |
Mpa |
ASTM D-790 | 3100 | 4000 | 7000 | 4600 |
Flexural Modulus(XD) |
Mpa |
1300 | 1500 | 2600 | 2400 |
B.without Micro Porous Layer and PTFE
Substrate with MPL&PTFE | Carbon paper | |||||
Measurement | Units | Method | N1S1007 | GDL240 | GDL260 | GDL340 |
Thickness | mm | TECLOCK SM-114 | 0.21 | 0.24 | 0.26 | 0.34 |
Basic weight | g/m2 | ASTM D-646 | 85 | 90 | 100 | 125 |
Air permeablity | sec | Gurley |
<225 |
<85 |
<200 |
<200 |
Through-Plane Resistance | mcm2 | Base on ASTM C-611 |
<15 |
<15 |
<10 |
<10 |
Tensile Strength(MD) | N/cm | ASTM D-828 | 35 | 30 | 37 | 45 |
Tensile Strength(XD) | N/cm | 17 | 18 | 33 | 36 | |
Flexural Modulus(MD) |
Mpa |
ASTM D-790 | 3100 | 4000 | 7000 | 4600 |
Flexural Modulus(XD) |
Mpa |
1300 | 1500 | 2600 | 2400 |
Read more about our Continuous carbonization Furnace for Carbon Fiber Papers.